С помощью метода вакуумно-дугового осаждения получены покрытия на основе (Ti - Zr - Nb)N. Изучены их физико-механические свойства и триботехнические характеристики. Коэффициент трения системы "покрытие - Al2O3" составляет 1,1. Покрытия характеризуются столбчатой структурой, твердость покрытий достигает НV0,05 = 44,57 ГПа.

By means of X-ray diffraction, transmission and scanning electron microscopy, energy dispersive spectroscopy and indentation methods, the effect of nitrogen atmosphere pressure on composition, structure and hardness of vacuum-arc (Ti - Al - Zr - Nb - Y)N coatings during the deposition process has been studied. The two-phase state of the coating with solid-solution metal component (bcc lattice) and nitride phase (fcc lattice) have been formed. Increasing the pressure of nitrogen atmosphere leads to the increase of nitrogen component in the coating as well as to increase of the ordering regions size, allowing to achieve the hardness of H = 49 GPa at a pressure of P = 0,5 Pa.

Зазначено, що нітриди перехідних металів Mo та Cr характеризуються порівняно низькою теплотою утворення. Вивчено можливості елементної та структурної інженерії вакуумно-дугових покриттів на основі Mo та Cr під впливом потенціалу зсуву Us і тиску реакційного газу PN. Виявлено, що за порівняно невеликої товщини шарів нанометрового порядку, який забезпечує надтвердий стан покриттів, подача Us величиною, що перевищує критичне значення, призводить до падіння твердості, що можна пояснити перемішуванням шарів міжфазної межі.