Phase and structural changes in polycrystal samples of Fe - AI - C alloy which are neccessary for getting of optimal durable and magnetic characteristics have been induced by quenching, cooling to - 196 <$E symbol Р >C, low temperature tempering or pulse laser irradiation. At that in the alloys a metastable phase-n-structure state with main peculiarity-presence in austenite and martensite matrix of an ordered carbide submicrovolumes of Fe4-yAlyCx which crystal lattice keep coherent to crystal lattices of matrix - have been formed. On primary stages of low temperature tempering in Fe - 4 wt. % Al - 2 wt. % С alloy the meaning of coercitive force is increasing and hardness of an alloy is decreasing. These changes have been explained by coherence breaking between crystal lattices of Kf submicrovolumes and <$E alpha >-martensite. It have been established that the analogous changes of magnetic properties in nearsurface layer about 1 mm can be induced.

Індекс рубрикатора НБУВ: К222.043 + К233.104.3

Рубрики:

Структурні і фазові перетворення в залізі та його сплавах. Теорія термічної обробки

Структурні та фазові перетворення в алюмінії та його сплавах. Теорія термічної обробки

Шифр НБУВ: Ж14161 Пошук видання у каталогах НБУВ 

---

  Якщо, ви не знайшли інформацію про автора(ів) публікації, маєте бажання виправити або відобразити більш докладну інформацію про науковців України запрошуємо заповнити "Анкету науковця"