The sintering of ceramic materials systems SiC - ZrB2, ZrB2 - ZrSi2 - SiC, ZrB2 - MoSi2 has been investigated. It has been shown that in the presence of zirconium and molybdenum disilicides sintering process is activated by the formation of a liquid phase. Increase in the SіC content in both types of composites (SiC - ZrB2, ZrB2 - ZrSi2 - SiC) raises their mechanical properties, while introduction of ZrSi2 to composites ZrB2 - SiC significantly increases their resistance to corrosion. Technological regimes of hot pressing of ceramic materials in the pilot production scale were developed. The set of parts of flame tube of the developed ceramic, which consists of plates measuring <$E 200~times~90~times~13> mm, was produced and delivered for testing to Pridneprovskaya Power Station (Dnepropetrovsk).

 Наукова періодика України 

---

Додаткова інформація про автора(ів) публікації:
(cписок формується автоматично, до списку можуть бути включені персоналії з подібними іменами або однофамільці)

• Григорьєв Олег Миколайович (1944–) (фізико-математичні науки)
• Скороход Владислав Валерійович (фізико-математичні науки)
• Скороход Валерій Володимирович (1934–2017) (технічні науки)
• Котенко Валерій Антонович (фізико-математичні науки)
• Коротєєв Олександр Володимирович (технічні науки)

  Якщо, ви не знайшли інформацію про автора(ів) публікації, маєте бажання виправити або відобразити більш докладну інформацію про науковців України запрошуємо заповнити "Анкету науковця"