By means of X-ray diffraction, transmission and scanning electron microscopy, energy dispersive spectroscopy and indentation methods, the effect of nitrogen atmosphere pressure on composition, structure and hardness of vacuum-arc (Ti - Al - Zr - Nb - Y)N coatings during the deposition process has been studied. The two-phase state of the coating with solid-solution metal component (bcc lattice) and nitride phase (fcc lattice) have been formed. Increasing the pressure of nitrogen atmosphere leads to the increase of nitrogen component in the coating as well as to increase of the ordering regions size, allowing to achieve the hardness of H = 49 GPa at a pressure of P = 0,5 Pa.

 Наукова періодика України 

---

Додаткова інформація про автора(ів) публікації:
(cписок формується автоматично, до списку можуть бути включені персоналії з подібними іменами або однофамільці)

• Соболь Олег Валентинович (фізико-математичні науки)
• Турбін Петро Васильович (1953–) (фізико-математичні науки)

  Якщо, ви не знайшли інформацію про автора(ів) публікації, маєте бажання виправити або відобразити більш докладну інформацію про науковців України запрошуємо заповнити "Анкету науковця"