Studenyak I. P. Compositional studies of optical parameters in (Ag3AsS3)x(As2S3)1-x (x = 0,3; 0,6; 0,9) thin films / I. P. Studenyak, M. Kranjcec, M. M. Kutsyk, Yu. O. Pal, Yu. Yu. Neimet, V. Yu. Izai, I. I. Makauz, C. Cserhati, S. Kokenyesi // Semiconductor Physics, Quantum Electronics and Optoelectronics. - 2016. - 19, № 4. - С. 371-376. - Бібліогр.: 20 назв. - англ.(Ag3AsS3)x(As2S3)1-x (x = 0,3; 0,6; 0,9) thin films were deposited onto a silica substrate by rapid thermal evaporation. The amount of Ag-rich crystalline phase precipitates on the surfaces of the films increases with Ag3AsS3 content. It has been shown that the absorption edge spectra are described by the Urbach rule. The temperature behaviour of absorption spectra was studied, the temperature dependences of energy position of absorption edge and Urbach energy were also investigated. The influence of compositional disordering due to Ag3AsS3 introduction into As2S3 on the optical parameters of (Ag3AsS3)x(As2S3)1-x thin films were analyzed. The spectral temperature and compositional behaviour of refractive index for (Ag3AsS3)x(As2S3)1-x thin films were studied. Індекс рубрикатора НБУВ: В372.6 + В377.1
Рубрики:
Шифр НБУВ: Ж16425 Пошук видання у каталогах НБУВ
Повний текст Наукова періодика України
![](/irbis_nbuv/images/info.png) Якщо, ви не знайшли інформацію про автора(ів) публікації, маєте бажання виправити або відобразити більш докладну інформацію про науковців України запрошуємо заповнити "Анкету науковця"
|