The paper presents the characteristics of the surface layer of d-elements of the IV group (titanium, zirconium and hafnium) after thermal diffusion saturation from a controlled oxygen-containing gas medium. Saturation was carried out at T = 750 <^>oC for <$E tau~=~5> hours at different pressures (P = 1,33 x 10<^>-1 Pa, P = 1,33 x 10<^>-2 Pa, P = 1,33 x 10<^>-3 Pa). Experimentally revealed differences in the characteristics of the surface layer of titanium, zirconium and hafnium. It was shown that a hardened diffuse layer is formed with a higher hardness relative to the metal core in the reverse order of their affinity for oxygen. On titanium, zirconium and hafnium, only a diffuse layer is formed without a phase film. The appearance of the surface of the samples before and after processing is given. According to the results of the study, chemical-thermal treatment in an oxygen-containing gas medium leads to changes in the surface layer of sheet material from titanium, zirconium and hafnium. The state of the surface layers directly affects the characteristics of finished products, in particular, fatigue life. Therefore, this treatment is a good tool for controlling the state of the surface layers of the aforementioned metals, and then their properties.

 Наукова періодика України 

---

Додаткова інформація про автора(ів) публікації:
(cписок формується автоматично, до списку можуть бути включені персоналії з подібними іменами або однофамільці)

• Труш Василь Степанович (технічні науки)
• Федірко Віктор Миколайович (1946–) (фізико-математичні науки)
• Стоєв Петро Ілліч (фізико-математичні науки)
• Тихоновський Михайло Андрійович (фізико-математичні науки)

  Якщо, ви не знайшли інформацію про автора(ів) публікації, маєте бажання виправити або відобразити більш докладну інформацію про науковців України запрошуємо заповнити "Анкету науковця"