This paper reports a study into the phase composition and microstructure of tungsten ore concentrate after carbon-thermal reduction at different O:C ratios in the charge. This is required for determining those indicators that reduce tungsten loss through the sublimation of oxide compounds when processing ore concentrates, as well as when using reduced tungsten-containing doping additives. The study results have established that the reduced tungsten concentrate at the O:C ratio in the charge within the interval of 1,33 - 2,30 contained the phases of W, W2C C, C, WO2. The microstructure demonstrated a spongy and disordered character. Together with W, the Mo, Si, Ca, Al impurities were present in the reduced products. The main elements identified at the sites studied had the following limiting content, % by weight: O - 5,01 - 17,32; C - 0,84 - 4,23; W - 61,21 - 86,78; Mo - 1,57 - 7,51; Si - 2,07 - 9,06; Ca - 1,34 - 11,30; Al - 0,27 - 0,40. The micro-inclusions at the examined surface areas acquired different complex shapes. There were traces of the process of caking between the particles. The analysis of the resulting data has shown that the most preferred ratio of O:C in the charge was 1,65. In this case, there is no lack of carbon and there is a predominance of W in the phase composition with a relatively little manifestation of the W2C phases, carbon, as well as the residual part of WO2. The post-reduction of the oxide component would occur during the doping process. The sponge structure contributes to a higher dissolution rate compared to standard tungsten ferroalloys. Lack of compounds with a relatively high propensity for sublimation does not require any special conditions to prevent the loss of tungsten in the gas phase, which increases the degree of assimilation of the target element.

 Наукова періодика України 

---

Додаткова інформація про автора(ів) публікації:
(cписок формується автоматично, до списку можуть бути включені персоналії з подібними іменами або однофамільці)

• Холодюк Олександр Володимирович (1976–) (технічні науки)
• Фесенко Галина Григорівна (1971–) (філософські науки)
• Фесенко Григорій Васильович (1941–) (технічні науки)

  Якщо, ви не знайшли інформацію про автора(ів) публікації, маєте бажання виправити або відобразити більш докладну інформацію про науковців України запрошуємо заповнити "Анкету науковця"