The paper presents the results of studies of the temperature dependences of the resistivity <$E rho>(T) and the Seebeck coefficient S(T) of binary structurally disordered alloys of the Ni1-xPx system. It was found that at 0,10 << x << 0,25 the absolute value of S(T) increases with phosphorus concentration and changes the sign, becoming positive at x >> 0,18. The resistivity <$E rho> increases with x, the temperature coefficient of electrical resistance - decreases and becomes negative, and S also increases and becomes positive near x = 0,18. These results agree with the Mooij correlation and the <$E rho>-S correlation for the studied samples, namely for samples with high resistivity S >> 0 and for samples with low resistivity - S << 0, which is observed in some nonmagnetic structurally disordered alloys. Thus, the Ni1-xPx system covers the range and behavior of electrokinetic characteristics that are characteristic of a few structurally disordered alloys. For x << 0,175 dependencies <$E rho>(T) and S(T) of the studied samples are similar to those observed in ferromagnetic structurally disordered iron-based alloys.

 Наукова періодика України 

---

Додаткова інформація про автора(ів) публікації:
(cписок формується автоматично, до списку можуть бути включені персоналії з подібними іменами або однофамільці)

• Яцишин Світлана Романівна (економічні науки)

  Якщо, ви не знайшли інформацію про автора(ів) публікації, маєте бажання виправити або відобразити більш докладну інформацію про науковців України запрошуємо заповнити "Анкету науковця"