Nickel foam is widely used as a current lead/current collector and as the base of nickel hydroxide electrodes for hybrid supercapacitors. An investigation of the influence of activation conditions for a commercial sample of nickel foam produced by Linyi Gelon LIB Co Ltd (China) was carried out using the method of impact nickel plating. The morphology of activated and non-activated nickel foam samples was investigated by scanning electron microscopy. Activated and non-activated nickel foam samples were investigated by methods of cyclic voltammetry and galvanostatic charge-discharge cycling in the supercapacitor mode. It was shown that upon activation at i = 1 A/dm<^>2 and <$E tau> = 10 min, a thin layer of porous nickel with incomplete coverage was formed. Activation with impact nickel at i = 7 A/dm<^>2 and <$E tau> = 3 min revealed the formation of a nickel coating with a highly developed surface, on which local cracks were found as a result of the accumulation of internal stresses. Activation with impact nickel at i = 1 A/dm<^>2 and <$E tau> = 10 min led to the formation of a coating with a highly developed surface, with significant peeling of the coating. Cyclic voltammetry showed high efficiency of impact nickel activation at i = 7 A/dm<^>2, <$E tau> = 3 min, and i = 20 A/dm<^>2, <$E tau> = 5 min. The specific current of the cathode peak increased 6,06 - 6,44 times with respect to the non-activated sample. The investigation of the activated samplesє electrochemical characteristics by the galvanostatic cycling method showed that impact nickel activation at i = 1 A/dm<^>2 and <$E tau> = 10 min was insufficient. It was found that at a discharge up to E = 0 V, the maximum specific capacitance of 0,731 F/cm<^>2 was obtained for samples activated by impact nickel at i = 7 A/dm<^>2 and <$E tau> = 3 min. The increase in specific capacitance compared to the non-activated sample was 4,49 times. At full discharge, the highest electrochemical activity was found for nickel foam samples activated by impact nickel at i = 20 A/dm<^>2 and <$E tau> = 5 min. The specific capacitance was 0,505 mA-h/cm<^>2, and it increased 9,02 times.

 Наукова періодика України 

---

Додаткова інформація про автора(ів) публікації:
(cписок формується автоматично, до списку можуть бути включені персоналії з подібними іменами або однофамільці)

• Коваленко Вячеслав Леонідович (ветеринарні науки)
• Коваленко Валентина Володимирівна (технічні науки)
• Коваленко Віталій Володимирович (національна безпека)
• Коваленко Віктор Вікторович (медичні науки)
• Коваленко Валентина Володимирівна (педагогічні науки)
• Коваленко Віталій Володимирович (1967–) (медичні науки)
• Коваленко Віталій Федосійович (біологічні науки)
• Коваленко Віталій Іванович (1980–) (технічні науки)
• Коваленко Валентина Миколаївна (1949–) (біологічні науки)
• Коваленко Валентина Михайлівна (філологічні науки)
• Коваленко Вячеслав Васильович (юридичні науки)
• Коваленко Валерія Олександрівна (економічні науки)
• Медяник Володимир Юрійович (технічні науки)

  Якщо, ви не знайшли інформацію про автора(ів) публікації, маєте бажання виправити або відобразити більш докладну інформацію про науковців України запрошуємо заповнити "Анкету науковця"